Crystal growth and properties of the disordered crystal Yb:SrLaAlO4: a promising candidate for high-power ultrashort pulse lasers

CrystEngComm Pub Date: 2018-05-31 DOI: 10.1039/C8CE00540K

Abstract

A high quality Yb3+-doped strontium lanthanum aluminate crystal, Yb:SrLaAlO4 (Yb:SLA) is grown by the Czochralski method. It is tetragonal (sp. gr. I4/mmm, a = b = 3.7536 ?, c = 12.6253 ?). Room- and low-temperature spectroscopy of Yb3+ ions in this crystal are studied. The Stark splitting is resolved. Absorption, stimulated-emission (SE) and gain cross-sections are determined with polarized light. In the spectral range of laser emission, the maximum σSE is 0.57 × 10?20 cm2 at 1047 nm for σ polarization. The polarized Raman spectra of Yb:SLA are presented. Thermal properties of Yb:SLA are characterized in terms of the linear thermal expansion, specific heat and thermal conductivity. The latter is as high as 6.06 and 4.30 W m?1 K?1 along the a- and c-axes, respectively (at room temperature). Broadband tuning of a continuous-wave (CW) Yb:SLA laser, from 1011 to 1082 nm has been achieved. Due to its good thermal properties, broad and smooth gain spectra, Yb:LSA is a promising material for power-scalable, broadly tunable CW and sub-100 fs mode-locked lasers at ～1 μm.

Graphical abstract: Crystal growth and properties of the disordered crystal Yb:SrLaAlO4: a promising candidate for high-power ultrashort pulse lasers
Recommended Literature