Hierarchically structured biphenylene-bridged periodic mesoporous organosilica?

Journal of Materials Chemistry Pub Date: 2011-10-06 DOI: 10.1039/C1JM12023A

Abstract

Novel composites of highly ordered and stable biphenyl-bridged periodic mesoporous organosilica (PMO) materials confined within the pores of anodic alumina membranes (AAM) were successfully synthesized by evaporation-induced self-assembly (EISA). 4,4′-Bis(triethoxysilyl)biphenyl (BTEBP) was used as a precursor in combination with the ionic surfactant cetyltrimethylammonium bromide (CTAB) or triblock-copolymer F127 as structure-directing agents. The resulting mesophases were characterized by small angle X-ray scattering (SAXS) and transmission electron microscopy (TEM). With ionic CTAB as a structure directing agent, samples with a mixture of the 2D-hexagonal columnar and a lamellar mesophase were obtained within the AAM channels. When using the nonionic surfactant F127, mesophases with a 2D-hexagonal circular structure were formed in the AAM channels. Additionally, a cubic Im[3 with combining macron]m phase could also be obtained with the same nonionic surfactant after the addition of lithium chloride to the precursor solution. The stability of both the circular and cubic biphenylene-bridged PMO against calcination temperatures of up to 250 °C was confirmed by NMR spectroscopy. Nitrogen sorption in the porous composite membrane shows typical type IV isotherms and narrow pore size distributions. All the biphenyl PMO/AAM composites show fluorescence due to the existence of biphenyl chromophores in the stable organosilica framework.

Graphical abstract: Hierarchically structured biphenylene-bridged periodic mesoporous organosilica
Recommended Literature