Investigation of the effect of polar functional groups on the crystal structures of indium MOFs?

CrystEngComm Pub Date: 2017-07-10 DOI: 10.1039/C7CE01067B

Abstract

Three new In-MOFs with –NH2 and/or –NO2 functionalities are reported using 2-amino- (H2BDC-NH2), 2-nitro- (H2BDC-NO2) and 2-amino-5-nitroterephthalic acid (H2BDC-NH2/NO2). Their structures were determined from single crystal X-ray diffraction data. The structure of the first In-MOF of composition [In(BDC-NH3)(BDC-NH2)]·1.6DMF·1.9H2O (In-BDC-NH2; DMF is dimethylformamide; the space group is P6222, a = b = 14.738(2) ? and c = 12.257(3) ?) is built up by two interpenetrating nets of InO8 polyhedra interconnected by BDC-NH22? ions to form a framework with qtz topology. Charge balance is accomplished by partial protonation of the amino group, which was confirmed by IR spectroscopy. The interpenetration leads to a decrease of the pore dimension (4.4 ? in diameter). Thermogravimetric analysis revealed stability up to 300 °C. Replacement of H2BDC-NH2 by H2BDC-NO2 in the reaction mixture led to the isoreticular MOF containing no –NO2 groups but exclusively un- and amino-functionalized linkers. Hence an indium mediated reduction of the H2BDC-NO2 linker molecule during solvothermal synthesis has occurred. The use of H2BDC-NH2/NO2 under exactly the same reaction conditions did not result in the formation of a MOF, but by changing the synthesis parameters, a new –NH2/–NO2 bifunctionalised In-MOF of composition (DMA)2[In3(μ3-O)(BDC-NH2/NO2)4.5]·DMF (DMA is dimethylammonium), denoted In-BDC-NH2/NO2, was obtained. The crystal morphology can be altered from cubic to truncated octahedral crystals by varying the DMF/ethanol volume ratio during synthesis. The compound crystallises in the cubic space group I[4 with combining macron]3m, a = 24.8947(1) ?, and the framework contains trinuclear {In3(μ3-O)} clusters which are interlinked by the BDC-NH2/NO22? ions to form super-tetrahedra. Four face-sharing super-tetrahedra form ultra-tetrahedra which are connected to form the final cubic framework with an ncb topology and isolated inaccessible pores.

Graphical abstract: Investigation of the effect of polar functional groups on the crystal structures of indium MOFs
Recommended Literature