Epitaxial (001) BiFeO3 thin-films with excellent ferroelectric properties by chemical solution deposition-the role of gelation?

Journal of Materials Chemistry C Pub Date: 2014-11-14 DOI: 10.1039/C4TC02371D

Abstract

High-quality phase-pure (001) epitaxial bismuth ferrite (BiFeO3; BFO) thin films have been realized by chemical solution deposition. A thorough chemical investigation of the precursor molecular changes during gelation reveals that control of the delicate balance between gelation and salt (metal nitrate) precipitation through solvent evaporation is the key to a homogenous gel, necessary to ultimately obtain high-quality films. Spin-coating at 3000 rpm for 30 seconds on a preheated STO(001) substrate (～70 °C) and subsequent heating at 90 °C leads to a suitable gel, which is then heated to 650 °C for crystallization. Pure phase BFO thin films of 150 nm thickness prepared by this route on lanthanum strontium manganite (La0.67Sr0.33MnO3; LSMO) buffered (001)-SrTiO3 (STO) substrates are shown to have not only epitaxial nature, but also robust ferroelectric properties with low coercive field. Critically, we show that these films can be achieved using stoichiometric 0.25 M precursors (with no Bi excess), thus obviating complexities typically arising from secondary phases associated with precursors having excess Bi. Square hysteresis loops with a high remanent polarization of 2Pr = 97.8 μC cm?2 and a low coercive field of 2Ec = 203.5 kV cm?1 are obtained at room temperature. Frequency-dependent hysteresis loops reveal a switching mechanism that is nucleation dominated. In addition, polarization direction dependent resistive switching behavior is also observed. The findings here thus show it is possible to realize high-quality bismuth ferrite thin films via chemical process techniques.

Graphical abstract: Epitaxial (001) BiFeO3 thin-films with excellent ferroelectric properties by chemical solution deposition-the role of gelation
Recommended Literature